You are correct re: no bondo... It will just melt away during the heat
stage.
I was told that lead or welded metal is best. Brass can be too soft.
Good luck.
Carl
> -----Original Message-----
> From: Dave Fain [SMTP:KC3565L@sprintmail.com]
> Sent: Wednesday, April 29, 1998 9:37 AM
> To: triumphs@autox.team.net
> Subject: Powder Coating-Generic question
>
>
> I am about to have a metal part (specifically a bicycle frame)
> media blasted and powder coated. I need to fill a small ding
> (about 1/8" deep) that cannot be easily removed. Am I correct
> in assuming that bondo would not be suitable for this? I was
> planning to use brass or lead, is one better than the other?
> I would prefer lead since I can work it with a regular propane
> torch. Yes, I know....gloves and adequate ventilation, etc.
> Thanks, Dave
|